BASF Ultramid® B50L 01 PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® B50L 01 PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid B50L 01 is a high-viscosity, lubricated, general-purpose extrusion PA6 grade. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or legislations for other countries will be provided on request.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Water Absorption	9.5 %	9.5 %	ISO 62
Moisture Absorption at Equilibrium	2.6 %	2.6 %	23°C/50% R.H.; ISO 62
Relative Viscosity	5.0 cP	5.0 cP	ISO Test; 96 % SAV
Viscosity Test	320 cm³/g	320 cm³/g	Viscosity number
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM Data; MD
Melt Flow	8.0 g/10 min @Load 5.00 kg, Temperature 275 °C	8.0 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	80.0 MPa	11600 psi	2 in/min; ASTM Test
	90.0 MPa	13100 psi	50mm/min; ISO 527
Elongation at Break	>= 50 %	>= 50 %	50mm/min, Nominal strain; ISO 527
Elongation at Yield	4.5 %	4.5 %	50mm/min; ISO 527
Tensile Modulus	3.00 GPa	435 ksi	1mm/min; ISO 527
	3.00 GPa	435 ksi	ASTM Test
Izod Impact, Notched	0.530 J/cm @Temperature -40.0 °C	0.993 ft-lb/in @Temperature -40.0 °F	ASTM Test
	1.34 J/cm @Thickness 3.17 mm	2.51 ft-lb/in @Thickness 0.125 in	ASTM Test
Charpy Impact Unnotched	NB	NB	ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.900 J/cm²	4.28 ft-lb/in²	ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	40.0 µm/m-°C @Temperature -30.0 - 30.0 °C	22.2 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
CTE, linear, Parallel to Flow	85.0 µm/m-°C	47.2 µin/in-°F	ISO 11359
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	160 °C	320 °F	ASTM Test
	160 °C	320 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	54.0 °C	129 °F	ASTM Test
	65.0 °C	149 °F	ISO 75
Vicat Softening Point	204 °C	399 °F	(50 °C/h / 50N) - B/50; ISO 306
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 60093
Dielectric Constant	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	IEC 60250
	4.0 @Frequency 100 Hz	4.0 @Frequency 100 Hz	IEC 60250
Dissipation Factor	0.023 @Frequency 1.00e+6 Hz	0.023 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	North America and Europe
FDA	21 CFR 177.1500
Form	Pellets
Impact Modified	No
Primary Processing Technique	Film Extrusion
Processing	Film Extrusion
	Profile Extrusion