BASF Ultramid® B3WG6 HP BK 23210 30% Glass Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3WG6 HP BK 23210 30% Glass Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade with enhances flowability used e.g. for automobile manifold.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Melt Flow 68 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 68 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
DIN 58765
Decomposition Temperature >= 300 °C
>= 572 °F
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed Zone
Zone 2 270 °C
518 °F
Compression
Zone 3 280 °C
536 °F
Metering-zone
Zone 4 280 °C
536 °F
Nozzle
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection Molding/Extrusion
280 °C
536 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Color BK 23210
Commercial Status Europe
Ignition Temperature >400°C
ASTM D1929
Peripheral screw speed < 0.3 m/s