BASF Ultramid® B3WG6 BK00564 BGVW 30% Glass Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3WG6 BK00564 BGVW 30% Glass Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3WG6 BK00564 BGVW is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 2.1 % | 2.1 % | 24 hour; ISO Test |
| 6.6 % | 6.6 % | ISO 62 | |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 180 MPa | 26100 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 177 MPa | 25700 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527 |
| Tensile Modulus | 8.83 GPa | 1280 ksi | ASTM Test |
| 10.5 GPa | 1520 ksi | 1mm/min; ISO 527 | |
| Flexural Modulus | 8.60 GPa | 1250 ksi | ISO Data |
| Izod Impact, Notched | 1.07 J/cm @Temperature -40.0 °C |
2.00 ft-lb/in @Temperature -40.0 °F |
ASTM Test |
| 1.50 J/cm @Thickness 3.17 mm |
2.81 ft-lb/in @Thickness 0.125 in |
ASTM Test | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM Test |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| 210 °C | 410 °F | ASTM Test |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK00564 BGVW | |
| Commercial Status | North America and Europe | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- RheTech Products GC43P250-00 43% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Natural
- PolyChem Alloy AquaGard™ 6004
- Nilit Nilamid A G10 FR PH1 50% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous)
- Gouda Vuurvast CURON 180 TF Dense Refractory Castable
- Saint-Gobain Chemfab® 5 High-Performance PTFE-Coated Glass
- SABIC Innovative Plastics LNP THERMOCOMP OC006 PPS - Linear (Europe-Africa-Middle East)
- AIM 63Sn/Pb37 Solder for Photonic Packaging
- Akzo Nobel Expancel® 091 DE 40 d30 Dry expanded microspheres
- Overview of materials for Polyethylene Terephthalate (PET), 30% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved