Industeel CLC 17.13.3 LN Nitrogen Containing 18Cr-10Ni-2Mo Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel , T S30000 Series Stainless Steel
Manufacturer Groupe Arcelor
Trade Name CLC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industeel CLC 17.13.3 LN Nitrogen Containing 18Cr-10Ni-2Mo Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: CLC 17-13-3LN is a nitrogen alloyed austenitic stainless steel with Mo additions. Its low carbon content avoids intergranular corrosion, even on welded pieces without an ulterior water quenching. Alloys CLC 17-13-3LN exhibits austenitic microstructure free of deleterious carbide precipitations in grain boundaries. The grade contains residual ferrite (= 2%) after solution annealing (1050 - 1150°C / 1922 - 2102°F) and water quenching. Higher Molybdenum content improves uniform and localized corrosion resistance. Nitrogen additions improve the structure stability and increase the yield strength compared to CLC 17-12-2L. Main properties of CLC 17-13-3LN are : high ductility, easy weldability, mirror polishability. Typical applications are food and beverage processing industry, chemical industry and chemical tankers.Information provided by manufacturer.
Physical Properties Metric English Comments
Density 7.95 g/cc
0.287 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 637 MPa
92400 psi
Typical
580 - 780 MPa
84100 - 113000 psi
Minimum Guaranteed
Tensile Strength, Yield >= 280 MPa

@Strain 0.200 %
 >= 40600 psi

@Strain 0.200 %
>= 320 MPa

@Strain 1.00 %
 >= 46400 psi

@Strain 1.00 %
355 MPa

@Strain 0.200 %
 51500 psi

@Strain 0.200 %
 Typical
Elongation at Break >= 45 %
>= 45 %
58 %
58 %
Typical
Creep Strength 270 MPa

@Temperature 600 °C,
Time 3.60e+6 sec
 39200 psi

@Temperature 1110 °F,
Time 1000 hour
Modulus of Elasticity 200 GPa

@Temperature 20.0 - 100 °C
 29000 ksi

@Temperature 68.0 - 212 °F
Poissons Ratio 0.299
0.299
Calculated
Shear Modulus 77.0 GPa

@Temperature 20.0 - 100 °C
 11200 ksi

@Temperature 68.0 - 212 °F
Charpy Impact >= 187 J
>= 138 ft-lb
325 J
240 ft-lb
Typical
>= 125 J

@Temperature -196 °C
 >= 92.2 ft-lb

@Temperature -321 °F
250 J

@Temperature -196 °C
 184 ft-lb

@Temperature -321 °F
 Typical
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature 20.0 - 100 °C
 8.89 µin/in-°F

@Temperature 68.0 - 212 °F
16.5 µm/m-°C

@Temperature 20.0 - 200 °C
 9.17 µin/in-°F

@Temperature 68.0 - 392 °F
17.0 µm/m-°C

@Temperature 20.0 - 300 °C
 9.44 µin/in-°F

@Temperature 68.0 - 572 °F
18.0 µm/m-°C

@Temperature 20.0 - 500 °C
 10.0 µin/in-°F

@Temperature 68.0 - 932 °F
Specific Heat Capacity 0.500 J/g-°C

@Temperature 20.0 - 100 °C
 0.120 BTU/lb-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 15.0 W/m-K

@Temperature 20.0 - 100 °C
 104 BTU-in/hr-ft²-°F

@Temperature 68.0 - 212 °F
Component Elements Properties Metric English Comments
Carbon, C 0.030 %
0.030 %
Chromium, Cr 17.9 %
17.9 %
Iron, Fe 68.51 %
68.51 %
As remainder
Molybdenum, Mo 2.6 %
2.6 %
Nickel, Ni 10.8 %
10.8 %
Nitrogen, N 0.16 %
0.16 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000750 ohm-cm

@Temperature 20.0 - 100 °C
 0.0000750 ohm-cm

@Temperature 68.0 - 212 °F