Premix Premi-Glas® 1100-20 Fiberglass Reinforced Thermoset BMC

Category	Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer	Premix
Trade Name	Premi-Glas®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Premi-Glas® 1100-20 Fiberglass Reinforced Thermoset BMC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Premi-Glas® 1100-20 is a fiberglass reinforced thermoset bulk molding compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent stiffness to weight ratio, non-meltingGood dimensional stability, including excellent thermal resistancePigmentable for molded-in color; best appearance with mold textureExcellent property retention in cold and hot environmentsGood corrosion resistance except in acid environments.Designed for compression or injection molding in matched metal die molds.Information provided by Premix.

Physical Properties	Metric	English	Comments
Specific Gravity	1.70 - 1.85 g/cc	1.70 - 1.85 g/cc
Linear Mold Shrinkage	0.0015 - 0.0035 cm/cm	0.0015 - 0.0035 in/in	Polymerization Shrinkage

Mechanical Properties	Metric	English	Comments
Tensile Strength	31.0 MPa	4500 psi	ASTM D638
Tensile Modulus	14.0 GPa	2030 ksi	ASTM D638
Flexural Strength	110 MPa	16000 psi	ASTM D790
Flexural Modulus	10.0 GPa	1450 ksi	ASTM D790
Poissons Ratio	0.30	0.30
Shear Modulus	5.40 GPa	783 ksi	Calculated
Izod Impact, Notched	4.25 J/cm	7.96 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.30 J/cm	9.93 ft-lb/in	ASTM D4812

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	35.0 µm/m-°C	19.4 µin/in-°F	Z Direction
CTE, linear, Transverse to Flow	25.0 µm/m-°C	13.9 µin/in-°F	XY Direction
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F

Processing Properties	Metric	English	Comments
Processing Temperature	150 °C	302 °F	Compression or Injection Molding
Clamp Pressure	3.45 - 6.89 MPa	500 - 1000 psi	Molding Pressure