BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3G8 BK00564 is a 40% glass filled, pigmented black, injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Water Absorption | 5.4 - 6.0 % | 5.4 - 6.0 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.6 - 2.0 % | 1.6 - 2.0 % | (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307 |
| Melt Flow | 78.65 g/10 min @Load 5.00 kg, Temperature 275 °C |
78.65 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 527 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 135 MPa | 19600 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 4.6 % | 4.6 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 8.20 GPa | 1190 ksi | ISO 527 |
| Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 10.5 J/cm² | 50.0 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 ohm-cm | 1.00e+8 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.0 @Frequency 1.00e+6 Hz |
6.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.13 @Frequency 1.00e+6 Hz |
0.13 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK00564 | |
| Commercial Status | North America and Europe | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Nylene® Norpex® AX20MR , 20% Mineral Reinforced Polyphenylene Ether
- Chevron Phillips 7109LT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- Ravago Manufacturing Americas Hylon® N1025HLFR Nylon 6/6 (DAM) (discontinued **)
- Saint-Gobain Norcrylâ„¢ A2000 Solid Acrylic Bonding Tape
- ThyssenKrupp XAR® PRIME Structural Steel
- ExxonMobil Bicor™ 30MB668 OPP Film
- ExxonMobil Spartan EP 100
- 3M 24S56W Automotive Protective Tape
- Arlon 56581R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved