- BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned)
BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 50% glass-fiber reinforced injection-molding grade with high heat aging resistance for technical articles of very high stiffness.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Water Absorption | 3.7 - 4.3 % | 3.7 - 4.3 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 1.0 - 1.4 % | 1.0 - 1.4 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 130 | 130 | ISO 307 |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | restricted |
| Melt Flow | 31.2 g/10 min @Load 5.00 kg, Temperature 275 °C |
31.2 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 180 MPa | 26100 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-1/-2 |
| Modulus of Elasticity | 12.5 GPa | 1810 ksi | ISO 527-1/-2 |
| Flexural Strength | 300 MPa | 43500 psi | at max force; ISO 178 |
| Flexural Modulus | 13.5 GPa | 1960 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.5 kJ/m² @Temperature 23.0 °C |
6.90 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 7800 MPa @Strain <=0.500 % |
1.13e+6 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.370 W/m-K | 2.57 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 260 °C | 500 °F | DIN 53765 |
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| 175 °C | 347 °F | for 50% loss of tensile strength after 5000hr | |
| 240 °C | 464 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.6 @Frequency 1.00 Hz |
6.6 @Frequency 1.00 Hz |
IEC 60250 |
| Dissipation Factor | 0.30 @Frequency 1.00e+6 Hz |
0.30 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Test solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK 00564 | |
| Commercial Status | Europe |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6310 Adhesive
- Lushan L-5R Polyethylene Copolymer Adhesive for Steel Pipe Coating
- Solvay Specialty Polymers Radel® R-7400 Polyphenylsulfone (PPSU)
- SABIC Innovative Plastics Valox® 8032UX PBT+PET (Asia Pacific)
- Techmer ES HiFill® PA6/6 GF50 HS L BK 50% Glass Filled (Conditioned)
- DSM Novamid® 2030CA PA666
- Aremco Ceramabind™ 644-S High Temperature Inorganic Binder
- 3M 2E93-EZ Protective Carpet Tapes
- Arlon 55571R028 0.028" (0.711 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Precision Polymer Engineering V60V Fluoroelastomer Compound
Copyright © lookpolymers.com All Rights Reserved