BASF Ultramid® 8281 HS PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 8281 HS PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 9.5 % | 9.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Measurement | 60 | 60 | Formic Acid |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | 2 in/min; ASTM Test | |
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 |
| 60 % | 60 % | 2 in/min; ASTM Test | |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM Test |
| 15.0 MPa @Temperature 120 °C |
2180 psi @Temperature 248 °F |
ASTM Test | |
| 15.0 MPa @Temperature 93.0 °C |
2180 psi @Temperature 199 °F |
ASTM Test | |
| 20.0 MPa @Temperature 65.0 °C |
2900 psi @Temperature 149 °F |
ASTM Test | |
| 175 MPa @Temperature -40.0 °C |
25400 psi @Temperature -40.0 °F |
ASTM Test | |
| Flexural Modulus | 1.04 GPa | 151 ksi | ASTM Test |
| 0.225 GPa @Temperature 120 °C |
32.6 ksi @Temperature 248 °F |
ASTM Test | |
| 0.240 GPa @Temperature 93.0 °C |
34.8 ksi @Temperature 199 °F |
ASTM Test | |
| 0.320 GPa @Temperature 65.0 °C |
46.4 ksi @Temperature 149 °F |
ASTM Test | |
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM Test |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Rotomolding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat | |
| UL.UL-C | Yes |
Users viewing this material also viewed the following:
- Quadrant EPP Nylatron® MC® 901 Blue, Heat Stabilized, Type 6 (ASTM Product Data Sheet)
- Radici Radilon® S CP300 (cond.) Nylon 6
- Fujipoly Industries Sarcon® 20GTR Thin-Film GTR
- Meilian Chemical PE-B1301 BLACK MASTERBATCH
- Karina E 06/923-IE MBU Blue Color Concentrate
- Samsung Cheil Industries Starex® BM-0320 J ABS, Unreinforced
- SABIC Innovative Plastics ULTEM AUT200 PEI
- Tisan TISLAMID® 66 30% Glass Fiber Reinforced Nylon 66
- Diamond Polymers ABS 9502
- DuPont Performance Polymers Rynite® FG530 NC011 Polyethylene Terephthalate (PET) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved