BASF Ultramid® 8202C HS BK-102 PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8202C HS BK-102 PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8202C HS BK-102 is a heat stabilized, low viscosity, pigmented black, PA6, injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in non-heat stabilized (Ultramid 8202C).

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	dry; ISO 1183
Water Absorption	1.6 %	1.6 %	24 hour; ISO Test
	9.3 %	9.3 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	2.6 %	2.6 %	beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity	2.6 cP	2.6 cP	ISO Test; 96 % SAV
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	43.0 MPa	6240 psi	50mm/min; ISO 527
Elongation at Break	>= 50 %	>= 50 %	50mm/min, Nominal strain; ISO 527
Elongation at Yield	22 %	22 %	50mm/min; ISO 527
Tensile Modulus	1.36 GPa	197 ksi	1mm/min; ISO 527

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Descriptive Properties	Value	Comments
Color	BK-102
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding
UL.UL-C	Yes