Styron MAGNUMâ„¢ 3416 SLG Acrylonitrile Butadiene Styrene (ABS) Resin

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	Styron
Trade Name	Magnum™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron MAGNUMâ„¢ 3416 SLG Acrylonitrile Butadiene Styrene (ABS) Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Overview: The mass (continuous process) ABS technology of Styron ensures an ABS resin that combines excellent processability with a stable light base color providing an ideal resin for self coloring. MAGNUM 3416 SLG is a new grade providing a unique property balance of ultra low gloss performance, excellent processing characteristics and high heat resistance.Applications: Unpainted automotive interior trim components with enhanced requirements on strength, stiffness and low creep performance also at elevated temperatures.Information provided by Styron

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/inÂ³	ISO 1183
Apparent Bulk Density	0.650 g/cc	0.0235 lb/inÂ³	ISO 60
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ISO 294-4
Melt Flow	8.5 g/10 min @Load 10.0 kg, Temperature 220 Â°C	8.5 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	39.0 MPa	5660 psi	ISO 527-2/50
Elongation at Break	60 %	60 %	ISO 527-2/50
Tensile Modulus	1.90 GPa	276 ksi	Injection Molded; ISO 527-2
Flexural Strength	62.0 MPa	8990 psi	3-point, 2 mm/min; ISO 178
Flexural Modulus	2.05 GPa	297 ksi	3-point, 2 mm/min; ISO 178
Charpy Impact, Notched	0.800 J/cmÂ² @Temperature -30.0 Â°C	3.81 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	1.20 J/cmÂ² @Temperature 23.0 Â°C	5.71 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	84.0 Â°C	183 Â°F	Unannealed; ISO 75-2/A
Vicat Softening Point	107 Â°C	225 Â°F	ISO 306/B50