Ashley Polymers Ashlene® 830LS-33G Nylon 6, 33% Glass Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	Ashley Polymers
Trade Name	Ashlene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ashley Polymers Ashlene® 830LS-33G Nylon 6, 33% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A 33% glass fiber reinforced and heat stabilized Nylon 6 designed to provide a high flexural modulus and good dimensional stability while maintaining the ease of processing associated with Nylon 6 type materials.Data provided by the manufacturer

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ASTM D792
Water Absorption	1.1 %	1.1 %	ASTM D570
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength, Ultimate	179 MPa	26000 psi	ATSM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Elongation at Yield	3.0 %	3.0 %	ASTM D638
Flexural Strength	235 MPa	34100 psi	ASTM D790
Flexural Modulus	9.30 GPa	1350 ksi	ASTM D790
Izod Impact, Notched	1.12 J/cm	2.10 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	216 °C	421 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	216 °C	421 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	216 °C	421 °F	ASTM D648