- BASF Novolen® 2900 H Polypropylene
BASF Novolen® 2900 H Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 2900 H Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molded and thermoformed parts.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| Tensile Modulus | 0.650 GPa | 94.3 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 9.50 J/cm² | 45.2 ft-lb/in² | |
| 1.70 J/cm² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 163 °C | 325 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.0 °C | 144 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | |
| Vicat Softening Point | 38.0 °C | 100 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.000070 @Frequency 100 Hz |
0.000070 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SF82TF20 Silver-coated Glass Fibers
- Premix Thermoplastics PRE-ELEC® CP 1319
- Park Electrochemical Nelcote® E-722 Epoxy Prepreg, 285 Kevlar® Reinforced
- NIZHNEKAMSKNEFTEKHIM PP 1452S (H39S) Propylene Homopolymer
- MarkeTech Repton EXP 36 Cordierite Mullite
- Saint-Gobain Rulon® 957 Grade Bearing/Seal PTFE
- Eagle Brass 302 Austenitic Stainless Steel, 1/8 Hardened
- ExxonMobil LDPE LD 160AT Low Density Polyethylene Resin
- 3M 8991L Polyester Tape
- Aardvark Polymers Aardalloy® 3326 POM Alloy Rotational Molding Resin
Copyright © lookpolymers.com All Rights Reserved