BASF Elastollan R 2002 25% Glass Filled TPUR

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer	BASF
Trade Name	Elastollan
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Elastollan R 2002 25% Glass Filled TPUR.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expansion comparable with steel and aluminum, low mold shrinkage and ease of painting. Typical Applications: Automotive body and rocker panels, underbody sealants, technical moldings e.g. plugs and ski tips.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.38 g/cc	0.0499 lb/in³	ISO 1183-1-A

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	70	70	ISO 686
Tensile Strength	70.0 MPa	10200 psi	50 mm/min; ISO 37
Elongation at Break	15 %	15 %	50 mm/min; ISO 37
Charpy Impact Unnotched	9.00 J/cm² @Temperature -30.0 °C	42.8 ft-lb/in² @Temperature -22.0 °F	DIN ISO 179
	13.0 J/cm² @Temperature 23.0 °C	61.9 ft-lb/in² @Temperature 73.4 °F	DIN ISO 179
Charpy Impact, Notched	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	DIN ISO 179
	4.00 J/cm² @Temperature 23.0 °C	19.0 ft-lb/in² @Temperature 73.4 °F	DIN ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	15.0 µm/m-°C @Temperature 23.0 - 80.0 °C	8.33 µin/in-°F @Temperature 73.4 - 176 °F	53752-A
Deflection Temperature at 0.46 MPa (66 psi)	170 °C	338 °F	DIN EN ISO 75-2/Be
Deflection Temperature at 1.8 MPa (264 psi)	130 °C	266 °F	DIN EN ISO 75-2/Ae

Processing Properties	Metric	English	Comments
Processing Temperature	225 - 245 °C	437 - 473 °F
Mold Temperature	50.0 - 70.0 °C	122 - 158 °F

Descriptive Properties	Value	Comments
Color	Black
Commercial Status	North America
Primary Processing Technique	Injection molding