BASF Elastollan B 80 A TPUR

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer	BASF
Trade Name	Elastollan
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Elastollan B 80 A TPUR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tensile strength, good damping and resilience performance and superior low temperature flexibility.Typical Applications: Sport-shoe soles and accessories, ski-boot shells, technical moldings, e.g. seals, castor tyres and tubing.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³	ISO 1183-1-A

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	82	82	ISO 868
Tensile Strength	40.0 MPa	5800 psi	after storage in water at 80°C for 42 days; ISO 37
	50.0 MPa	7250 psi	ISO 37
	2.00 MPa @Strain 20.0 %	290 psi @Strain 20.0 %	ISO 37
	5.00 MPa @Strain 100 %	725 psi @Strain 100 %	ISO 37
	14.5 MPa @Strain 300 %	2100 psi @Strain 300 %	ISO 37
Elongation at Break	600 %	600 %	ISO 37
	600 %	600 %	after storage in water at 80°C for 42 days; ISO 37
Charpy Impact, Notched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DIN EN ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	DIN EN ISO 179
Tear Strength	85.0 kN/m	485 pli	DIN ISO 34-1/Bb
Abrasion	35	35	[mm<sup>3</sup>; ISO 4649
Compression Set	20 % @Temperature 23.0 °C	20 % @Temperature 73.4 °F	ISO 815
	30 % @Temperature 70.0 °C	30 % @Temperature 158 °F	ISO 815

Processing Properties	Metric	English	Comments
Processing Temperature	175 - 230 °C	347 - 446 °F	Injection molding
Mold Temperature	20.0 - 70.0 °C	68.0 - 158 °F

Descriptive Properties	Value	Comments
Commercial Status	North America
Primary Processing Technique	Injection molding