Azoty Tarnow™ TARNOFORM 300 K POM
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARNOFORM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARNOFORM 300 K POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tribological modified grade with addition of special chalk, which causes decrease of wear.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Melt Flow | 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ISO 2039-2 |
| Ball Indentation Hardness | 157 MPa | 22800 psi | 358 N; ISO 2039-1 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 45 % | 45 % | ISO 527 |
| Flexural Strength | 66.0 MPa | 9570 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | 1A; ISO 180 |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | 1eA; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.48 J/g-°C | 0.354 BTU/lb-°F | |
| Melting Point | 167 °C | 333 °F | 10°C/min.; ISO 3146 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | ISO 75 |
| Vicat Softening Point | 157 °C | 315 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.1 @Frequency 1e+6 Hz |
4.1 @Frequency 1e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.0095 @Frequency 1e+6 Hz |
0.0095 @Frequency 1e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 230 °C | 356 - 446 °F | Barrel temperature |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA - 51 KC General Purpose Acrylic Resin
- Lehmann & Voss LUVOCOM® 1/CF/10/GF/20/BK Polyamide 66, with carbon fiber and glass fiber, heat stabilized
- SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS (Asia Pacific)
- Teknor Apex Sinpolene CPP1050 Polypropylene
- Master Bond Supreme 46HT-2 Toughened, High Shear and Peel Strength Adhesive
- Chase Plastics CP Pryme® NN100HL (Dry) Nylon 66, Heat Stabilized, Lubricated
- Plenco 6582 Phenolic, Briquette, Injection Molded
- DuPont Performance Polymers Crastin® CE15315 BK010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- Eurotec® Tecomid® NB40 MR30 NL PA 6 30% mineral reinforced
Copyright © lookpolymers.com All Rights Reserved