- Ashley Polymers Ashlene® 528LW Nylon 66
Ashley Polymers Ashlene® 528LW Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 528LW Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose injection molding grade.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % | 1.5 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 81.0 MPa | 11700 psi | ATSM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.032 GPa | 439.8 ksi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 |
| Shear Strength | 65.0 MPa | 9430 psi | ASTM D732 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | |
| Melting Point | 255 °C | 491 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Brittleness Temperature | -79.0 °C | -110 °F | ASTM D746 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Eastman 5282 LDPE 8% EVA Copolymer, High Clarity, High Impact Film Resin (discontinued **)
- Hogen Duralloy H30W 80 Tungsten/20 Copper PM Metal Composite
- Karina 550D02/101-AT-IS Yellow PVC Compound
- Westlake Epolene® N-21P Nonemulsifiable - Low Molecular Weight Polyethylene Polymer
- Toyobo Pelprene™ P-70B Polyester TPE
- ConocoPhillips Syncon® 680 Synthetic EP Gear Oil, AGMA No. 8EP
- BASF Lupranate® 5030 Isocyanate
- Ashley Polymers Ashlene® 630-33G Nylon 6, 33% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved