Ashley Polymers Ashlene® 527LD-13G Nylon 66, 13% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 527LD-13G Nylon 66, 13% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A high impact 13% glass reinforced Nylon 66.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.90 % | 0.90 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ATSM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| Izod Impact, Notched | 1.55 J/cm | 2.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 254 °C | 489 °F | ASTM D3418 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T700 12K 2x2 Twill Reinforced
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 70 PHR N550 (FEF) Filler
- Arlon 48571R005 0.0055" (0.140 mm) Uncured Silicone Rubber with Fiberglass Substrate (discontinued **)&l
- SABIC Innovative Plastics NORYL 731S PPE+PS (Asia Pacific)
- Unipetrol Propylene for Polymerization
- Toho Tenax Tenax® HTA 5131 Chopped Carbon Fiber
- ConocoPhillips Tacna® M5 Grease NLGI Grade 1
- Eurostar Staramide BG6ST01 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
- 3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive
Copyright © lookpolymers.com All Rights Reserved