- Ashley Polymers Ashlene® 264-15 PPO, 15% Glass Reinforced
Ashley Polymers Ashlene® 264-15 PPO, 15% Glass Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 264-15 PPO, 15% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A general purpose, 15% glass reinforced PPO resin for injection molding applications.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ATSM D638 |
| Elongation at Break | 5.1 % | 5.1 % | ASTM D638 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Karina 550D32/13-AT-IS Orange PVC Compound
- Mikro-Technik Reproflon G25 PTFE
- Saint-Gobain CHR® SG03-10(R) Premium Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Sawbones Second-Generation Simulated Cancellous Bone (Solid)
- A. Schulman PP 1407L-01 Polypropylene High-Impact Copolymer Polypropylene
- ChevronTexaco SAE 40 Military Symbol 9250 Engine Oil
- Ashley Polymers Ashlene® ABS Resin F-214
- Axiall 1275 Plenum Flexible PVC
Copyright © lookpolymers.com All Rights Reserved