Ascend Performance Materials Vydyne® 65A Nylon 66, General Purpose, intermediate viscosity, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 65A Nylon 66, General Purpose, intermediate viscosity, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 65A is a medium-viscosity, heat-stabilized PA66 resin suitable for injection-molding extrusion and compounding applications. It is available in natural color only. Vydyne 65A resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles.Availability:Asia PacificEuropeNorth AmericaAdditive: Heat StabilizerSlip Features:General PurposeGood Chemical ResistanceGood ToughnessHeat StabilizedHigh RigidityHigh StrengthMedium ViscosityOil ResistantSolvent ResistantUses:Industrial ApplicationsMonofilamentsProfilesRodsSheetTubingAppearance: Natural ColorForms: PelletsProcessing Method: Extrusion and Injection MoldingInformation provided by Ascend
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ISO 1183
Water Absorption 8.5 %
8.5 %
24 hrs; ISO 62
Moisture Absorption at Equilibrium 2.5 %
2.5 %
Equilibrium at 50%rh; ISO 62
Linear Mold Shrinkage 0.020 cm/cm

@Thickness 2.00 mm
0.020 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.018 cm/cm

@Thickness 2.00 mm
0.018 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527-2
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527-2
Elongation at Break >= 200 %
>= 200 %
ISO 527-2
Elongation at Yield 21 %
21 %
ISO 527-2
Tensile Modulus 1.80 GPa
261 ksi
ISO 527-2
Flexural Strength 20.0 MPa
2900 psi
ISO 178
Flexural Modulus 0.700 GPa
102 ksi
ISO 178
Izod Impact, Notched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
ISO 180
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Descriptive Properties Value Comments
Blown Film Bath Temperature 20-80°C
Chill Roll Temperature (Cast Film) 20-80°C