Ascend Performance Materials Vydyne® 50BW Nylon 66, Conditioned (2.5% Moisture)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 50BW Nylon 66, Conditioned (2.5% Moisture).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 50BW is a general purpose Nylon 66 resin. Available in natural. Designed for extrusion applications that do not require use of a high-viscosity resin. This resin offers a well-balanced combination of engineering properties characterized by high strength, rigidity, good toughness, high melt point, good surface lubricity, and abrasion resistance. Vydyne 50BW maintains the chemical resistance typical of nylon to many chemicals, solvents, gasoline, and machine and motor oils. Vydyne 50BW permits the manufacture of parts with good initial color plus good property and color retention when using regrind. This resin is recognized by Underwriters Laboratories and conforms to the requirements of many industrial, federal, and military specifications for premium-quality general-purpose Nylon 66 resins. Typical Applications/End Uses. Vydyne 50BW has been successfully extruded in applications that do not require high melt strength, such as monofilament and bristle products.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ISO 1183
Water Absorption 1.3 %

@Time 86400 sec
1.3 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.4 %
2.4 %
50% RH; ISO 62
Linear Mold Shrinkage 0.012 cm/cm

@Thickness 2.00 mm
0.012 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm

@Thickness 2.00 mm
0.014 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 56.0 MPa
8120 psi
ISO 527
Elongation at Break >= 100 %
>= 100 %
ISO 527
Elongation at Yield 20 %
20 %
ISO 527
Tensile Modulus 1.40 GPa
203 ksi
ISO 527
Flexural Strength 20.0 MPa
2900 psi
ISO 178
Flexural Modulus 1.36 GPa
197 ksi
ISO 178