Ascend Performance Materials VYDYNE® R400G Nylon, Mineral and Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | Ascend Performance Materials (formerly Solutia) |
| Trade Name | VYDYNE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ascend Performance Materials VYDYNE® R400G Nylon, Mineral and Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical property data. VYDYNE is a registered trademark of Solutia Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.80 % | 0.80 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.010 cm/cm | 0.0050 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 6.70 GPa | 972 ksi | D638 |
| Flexural Yield Strength | 184 MPa | 26700 psi | ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM D790 |
| Poissons Ratio | 0.26 @Temperature -40.0 °C |
0.26 @Temperature -40.0 °F |
|
| 0.38 @Temperature 23.0 °C |
0.38 @Temperature 73.4 °F |
||
| 0.42 @Temperature 66.0 °C |
0.42 @Temperature 151 °F |
||
| 0.47 @Temperature 121 °C |
0.47 @Temperature 250 °F |
||
| Shear Modulus | 2.43 GPa | 352 ksi | Calculated |
| Izod Impact, Notched | 0.400 J/cm @Thickness 3.17 mm |
0.749 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction | 0.26 | 0.26 | ASTM D1894 |
| Coefficient of Friction, Static | 0.34 | 0.34 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 31.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
17.2 µin/in-°F @Temperature -40.0 - 180 °F |
|
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | Mfr. internal test |
| Thermal Conductivity | 0.390 W/m-K | 2.71 BTU-in/hr-ft²-°F | Mfr. internal test |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 3.17 mm |
424 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Eastman 1810E Polyethylene (discontinued **)
- Cookson Group Plaskon® 150.401 Encapsulation Resin (discontinued **)
- LG Chemical B320 EPS, Non-Flame Retardant
- Techmer ES Luriblend® TPX-POM-01060
- Engineered Syntactic Systems AZ-38 Deep Water Syntactic Foam
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.25 PHR Zinc Stearate
- Dow Corning Z-2306 SILANE
- CP-Polymer-Technik Wellamid® 6000 GV 10 HWCP 10% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- CLAL-MSX NICLAFOR® 1000 TD1 Quenched/Cold Rolled, Drawn Copper Alloy
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N774 Filler
Copyright © lookpolymers.com All Rights Reserved