Arlon UltraPad™ 51073R031D Silicone-Based Press Pad

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name	Ultrapad™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon UltraPad™ 51073R031D Silicone-Based Press Pad.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

UltraPad™ D65: Silicone Based Press PadDesign/Construction:Interleave: 3 mil PolyethyleneSide 1: Cured Silicone RubberSubstrate: Style 7628 FiberglassSide 2: Cured Silicone RubberThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Density	1.09 g/cc	0.0394 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	211 microns	8.30 mil	Substrate; Arlon SQA-TMS-003
	290 microns	11.4 mil	Side 1; Arlon SQA-TMS-003
	290 microns	11.4 mil	Side 2; Arlon SQA-TMS-003
	790 microns	31.1 mil	Overall Thickness; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	43	43	Silicone Property; ASTM D2240
	81	81	Product Property; ASTM D2240
Tensile Strength	7.79 MPa	1130 psi	Silicone Property; ASTM D412
Elongation at Break	850 %	850 %	Silicone Property; ASTM D412

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	150 - 300 °C @Pressure 0.000 - 5.00 MPa	302 - 572 °F @Pressure 0.000 - 725 psi	Recommended Application Range

Processing Properties	Metric	English	Comments
Shelf Life	60.0 Month @Temperature 22.8 °C	60.0 Month @Temperature 73.0 °F

Descriptive Properties	Value	Comments
Color	Red
Service Life	114 hours	at 225°C and 2.07 MPa
Total Product Weight (oz/yd2)	26.2	Arlon SQA-TMS-025