- HOME
- POLYMER SEARCH
- Thermoplastic
- ABS Polymer
- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Samsung Cheil Industries Starex® LH-0300 ABS, Unreinforced Heat Resistant
Samsung Cheil Industries Starex® LH-0300 ABS, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® LH-0300 ABS, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0042 cm/cm @Thickness 3.20 mm |
0.0042 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0048 cm/cm @Thickness 3.20 mm |
0.0048 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 32.5 MPa | 4710 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 34.7 MPa | 5040 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 51 % | 51 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.7327 GPa | 251.31 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 45.6 MPa | 6610 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.7253 GPa | 250.23 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 6.35 mm |
1.84 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.47 J/cm @Thickness 3.17 mm |
2.76 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 71 T 10 PP, 10% mineral filling
- Polimeri Europa Flexirene® MT 40 A Linear Low Density Polyethylene
- PTS Trimid® N6-M200HL Impact Modified Heat Stabilized Nylon 6 with Lube
- MarkeTech 95-3-2 Tungsten Alloy, AMS-T-21014 Class 3
- SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS
- BNZ Materials BNZ-23A Insulating Firebrick
- Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 900 (Age-Hardened 482°C/1hr/AC)
- PolyOne Edgetek® NI-30CF/000 Nylon 6/10 - 30% Carbon Fiber Reinforced (discontinued **)
- 3A Composites Core Materials AIREX® C70.48 Universal Structural Foam
Copyright © lookpolymers.com All Rights Reserved