Arlon IsoClad 933 Non-Woven Fiberglass Reinforced PTFE
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Arlon |
| Trade Name | IsoClad |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon IsoClad 933 Non-Woven Fiberglass Reinforced PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Traditional - Highest Performance, PTFE Coated Light Woven Glass Styles, Interdispersed PTFE FilmInformation provided by Arlon Materials for Electronics (MED).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.27 g/cc | 0.0820 lb/in³ | |
| Water Absorption | 0.050 % | 0.050 % | |
| Outgassing - Total Mass Loss | 0.00 % | 0.00 % | Collected Volatile |
| 0.030 % | 0.030 % | Total Mass Loss |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Peel Strength | 1.75 kN/m | 10.0 pli |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 31.0 µm/m-°C | 17.2 µin/in-°F | x direction |
| 35.0 µm/m-°C | 19.4 µin/in-°F | y direction | |
| CTE, linear, Transverse to Flow | 203 µm/m-°C | 113 µin/in-°F | z direction |
| Thermal Conductivity | 0.263 W/m-K | 1.83 BTU-in/hr-ft²-°F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.33 @Frequency 1.00e+10 Hz |
2.33 @Frequency 1.00e+10 Hz |
|
| 2.33 @Thickness 0.127 mm |
2.33 @Thickness 0.00500 in |
||
| 2.33 @Thickness 1.52 mm |
2.33 @Thickness 0.0600 in |
||
| Dissipation Factor | 0.0016 @Frequency 1.00e+10 Hz |
0.0016 @Frequency 1.00e+10 Hz |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Temperature Coefficient of Dielectric (ppm/°C) | -132 |
Users viewing this material also viewed the following:
- Raschig Group RALUPOL® 804 UP Polyester
- Kazanorgsintez 102-12K Cable Composition Based on Low Density Polyethylene
- Magyar Aluminum ALOLT 01 Aluminum Hydroxide
- LG Chemical MA210 ABS, Low Gloss
- Karina 06/846-FC-LMP (SDB) Blue Color Concentrate for PVC
- Henkel Hysol Benzoxazine 99110 Infusion Resin
- Universal Wire Works BAg-13-A (AMS 4765) Silver Brazing Filler Metal
- A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound
- Ensinger HYDEX® 4101 Polybutylene Terephthalate (PBT)
- Arlon 44570R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved