Arlon AD300C Commercial Microwave and RF Laminate Material

Category Polymer , Thermoset
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon AD300C Commercial Microwave and RF Laminate Material.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent Thermal Coefficient of Dielectric Constant (TCEr = -25 ppm/°C)Excellent PIM performanceHigh Thermal Conductivity ideal for Higher Power DesignsReduced Coefficient of Thermal Expansion in z-direction (CTEz)Cost-effective Advanced Material for Commercial RF Applications and High Volume Manufacturing DesignTightest Commercial Laminate DK Tolerance for Impedance ControlBenefits:Low Dielectric Loss (Loss Tangent)Lower Insertion Loss (S21)Excellent Electrical Phase Stability vs. TemperatureExcellent Copper Bond StrengthLow Moisture AbsorptionTypical Applications:Base Station AntennasPower Amplifiers (PA), Tower Mounted Amplifiers (TMA) and Tower Mounted Booster Amplifiers (TMB)Antenna Feed NetworksRF Passive ComponentsMultimedia Transmission SystemsInformation provided by Arlon Materials for Electronics (MED).
Physical Properties Metric English Comments
Density 2.07 g/cc
0.0748 lb/in³
ASTM D792 Method A
Water Absorption 0.060 %
0.060 %
IPC TM-650 2.6.2.1
Mechanical Properties Metric English Comments
Tensile Strength 40.7 MPa
5900 psi
Machine; IPC TM-650 2.4.18.3
52.4 MPa
7600 psi
Cross; IPC TM-650 2.4.18.3
Modulus of Elasticity 3.86 GPa
560 ksi
IPC TM-650 2.4.18.3
Flexural Strength 68.9 MPa
10000 psi
Machine; IPC TM-650 2.4.4
89.6 MPa
13000 psi
Cross; IPC TM-650 2.4.4
Poissons Ratio 0.26
0.26
ASTM D3039
Peel Strength >= 1.75 kN/m
>= 10.0 pli
To Copper (1 oz./35 micron); After Thermal Stress; IPC TM-650 2.4.8
>= 1.75 kN/m
>= 10.0 pli
To Copper (1 oz./35 micron); At Elevated Temperatures; IPC TM-650 2.4.8.2
2.10 kN/m
12.0 pli
To Copper (1 oz./35 micron); After Process Solutions; IPC TM-650 2.4.8
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C

@Temperature 50.0 - 150 °C
5.00 µin/in-°F

@Temperature 122 - 302 °F
x direction; IPC TM-650 2.4.41
15.0 µm/m-°C

@Temperature 50.0 - 150 °C
8.33 µin/in-°F

@Temperature 122 - 302 °F
y direction; IPC TM-650 2.4.41
CTE, linear, Transverse to Flow 54.0 µm/m-°C

@Temperature 50.0 - 150 °C
30.0 µin/in-°F

@Temperature 122 - 302 °F
z direction; IPC TM-650 2.4.24
Thermal Conductivity 0.500 W/m-K
3.47 BTU-in/hr-ft²-°F
ASTM E1461
Decomposition Temperature 500 °C
932 °F
Onset; IPC TM-650 2.4.24.6
555 °C
1030 °F
5 percent; IPC TM-650 2.4.24.6
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.20e+14 ohm-cm
1.20e+14 ohm-cm
C96/35/90; IPC TM-650 2.5.17.1
1.90e+14 ohm-cm
1.90e+14 ohm-cm
E24/125; IPC TM-650 2.5.17.1
Surface Resistance 2.50e+14 ohm
2.50e+14 ohm
C96/35/90; IPC TM-650 2.5.17.1
7.70e+14 ohm
7.70e+14 ohm
E24/125; IPC TM-650 2.5.17.1
Dielectric Constant 2.97

@Frequency 1.00e+6 Hz
2.97

@Frequency 1.00e+6 Hz
may vary by thickness; IPC TM-650 2.5.5.3
2.97

@Frequency 1.00e+10 Hz
2.97

@Frequency 1.00e+10 Hz
may vary by thickness; IPC TM-650 2.5.5.5
Dielectric Strength 16.9 kV/mm
430 kV/in
IPC TM-650 2.5.6.2
Dielectric Breakdown 30000 V
30000 V
IPC TM-650 2.5.6
Dissipation Factor 0.0014

@Frequency 1.00e+6 Hz
0.0014

@Frequency 1.00e+6 Hz
IPC TM-650 2.5.5.3
0.0020

@Frequency 1.00e+10 Hz
0.0020

@Frequency 1.00e+10 Hz
IPC TM-650 2.5.5.5
Arc Resistance >= 180 sec
>= 180 sec
IPC TM-650 2.5.1
Descriptive Properties Value Comments
IPC Delamination - T260 (minutes) >60
IPC TM-650 2.4.24.1
IPC Delamination - T288 (minutes) >60
IPC TM-650 2.4.24.1
IPC Delamination - T300 (minutes) >60
IPC TM-650 2.4.24.1
Temperature Coefficient of Dielectric (ppm/°C) -25
IPC TM-650 2.5.5.5; at 10 GHz (-40 - 150°C)