Arlon 44981R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 44981R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Interleave 1: Polyethylene Side 1: Uncured Silicone Rubber Substrate: Style 1165 FiberglassSide 2: Uncured Silicone Rubber Interleave 2: Polyethylene UL Recognition File: E54153Product Use: Flexible heater substrateAppearance: Red colored, high viscosity gum on fiberglass clothThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.57 g/cc	0.0567 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	127 microns	5.00 mil	Side 1; Arlon SQA-TMS-003
	127 microns	5.00 mil	Side 2; Arlon SQA-TMS-003
	127 microns	5.00 mil	Substrate; Arlon SQA-TMS-003
	381 microns	15.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	72	72	Silicone Property; ASTM D2240
Tensile Strength	4.83 MPa	700 psi	Silicone Property; ASTM D412
Elongation at Break	190 %	190 %	Silicone Property; ASTM D412
Peel Strength	0.614 kN/m	3.50 pli	Bond Strength; Arlon SQA-TMS-011

Thermal Properties	Metric	English
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
UL RTI, Electrical	150 °C	302 °F
UL RTI, Mechanical without Impact	150 °C	302 °F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Dielectric Strength	39.4 kV/mm	1000 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 121 °C	0.250 hour @Pressure 50.0 psi, Temperature 250 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 21.1 °C	6.00 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
	Red	Substrate
Total Product Weight (oz/yd2)	18.4	Arlon SQA-TMS-025

Users viewing this material also viewed the following: