Arkema Group Rilsan® BESN TL Nylon 11, Rigid Tubing Grade (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Unreinforced
Manufacturer	Arkema
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® BESN TL Nylon 11, Rigid Tubing Grade (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation ISO 1874-PA11,EHL,22-010Rigid grade for tubes extrusion. Available colors: black and natural. Light and heat stabilized.High impact strength. High burst pressure. Good chemical resistance. Ability to be processed at high speed. Easy to color (sublimation).Example applications: Pneumatic suspension line.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.03 g/cc	0.0372 lb/in³
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 235 °C	1.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	42.0 MPa	6090 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	8.0 %	8.0 %	50 mm/min
Tensile Modulus	1.26 GPa	183 ksi	1 mm/min
Charpy Impact Unnotched	NB	NB
	NB	NB	Low Temp
Charpy Impact, Notched	1.49 J/cm²	7.09 ft-lb/in²
	1.32 J/cm² @Temperature -30.0 °C	6.28 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	85.0 µm/m-°C @Temperature 20.0 °C	47.2 µin/in-°F @Temperature 68.0 °F
Melting Point	183 °C	361 °F	(Dry)
Deflection Temperature at 0.46 MPa (66 psi)	145 °C	293 °F
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F
Vicat Softening Point	160 °C	320 °F	50°C/hr; 50N
Flammability, UL94	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in
	V-2 @Thickness 3.20 mm	V-2 @Thickness 0.126 in
Oxygen Index	25 %	25 %

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Strength	30.0 kV/mm	762 kV/in