Arkema Group Rilsan® BECN P20 TL Nylon 11 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Unreinforced |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® BECN P20 TL Nylon 11 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Water Absorption | 1.8 % | 1.8 % | |
| Melt Flow | 11.9 g/10 min @Load 2.16 kg, Temperature 235 °C |
11.9 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 34 % | 34 % | 50 mm/min |
| Tensile Modulus | 0.525 GPa | 76.1 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.000348 @Frequency 1e+6 Hz |
0.000348 @Frequency 1e+6 Hz |
|
| 0.000486 @Frequency 100 Hz |
0.000486 @Frequency 100 Hz |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPC-20T Nat Polypropylene Copolymer (PP Copolymer)
- SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp PF00A PA 6 (Europe-Africa-Middle East)
- Teknor Apex Monprene® MP 1128 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Hot Pink 50377 Concentrate Based In Polyethylene
- Hexcel® HexPly® EF02 Epoxy Curing System after THR 120 EF01 S50 37% Curing Cycle
- Alloy Wire International RW 70 Hot Cutting Wire - High Strength
- Polykemi AB POLYfill PPHC K8030 Polypropylene, Mineral Reinforced
- BASF Ultramid® B3S HP PA6 (Dry)
- Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched
Copyright © lookpolymers.com All Rights Reserved