3M Scotch-Weld™ DP8005 Translucent Structural Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ DP8005 Translucent Structural Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8005 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of polypropylene, polyethylene, and TPO’s without special surface preparation. It can replace screws, rivets, plastic, welding, and two-step processes which include chemical etchants, priming or surface treatments in many applications.Information provided by 3M

Physical Properties	Metric	English	Comments
Brookfield Viscosity	17000 - 30000 cP	17000 - 30000 cP	Base, DV-II, #7 sp, 20 rpm
	35000 - 55000 cP	35000 - 55000 cP	Acecelerator, DV-II, #7 sp, 20 rpm

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	55	55	ASTM D2240
Tensile Modulus	0.59067 GPa	85.669 ksi	at 1% Strain
Shear Strength	0.172 MPa	25.0 psi	Overlap, Toluene, Cohesive Failure
	0.689 MPa	100 psi	Overlap, Acetone, Cohesive Failure
	1.72 MPa	250 psi	Overlap, PTFE, Adhesive Failure
	2.24 MPa	325 psi	Overlap, Gasoline, Cohesive Failure
	2.76 MPa	400 psi	Overlap, LDPE, Substrate Failure
	3.79 MPa	550 psi	Overlap, HIPS, Substrate Failure
	4.48 MPa	650 psi	Overlap, Glass (3/16" thick), Substrate Failure
	5.17 MPa	750 psi	Overlap, UHMWPE, Substrate Failure
	5.34 MPa	775 psi	Overlap, Polystyrene, Substrate Failure
	5.86 MPa	850 psi	Overlap, Polycarbonate, Substrate Failure
	6.38 MPa	925 psi	Overlap, 71°C/100% RH salt water soak for 14 days, Cohesive Failure
	6.55 MPa	950 psi	Overlap, Plexiglass (PMMA), Substrate Failure
	6.55 MPa	950 psi	Overlap, HDPE/Galvanealed, Adhesive Failure
	6.55 MPa	950 psi	Overlap, HDPE/CRS, Adhesive Failure
	6.55 MPa	950 psi	Overlap, 71°C/100% RH for 14 days, AF/CF
	6.55 MPa	950 psi	Overlap, Isopropyl Alcohol, Substrate Failure
	6.72 MPa	975 psi	Overlap, HDPE/HDG, Adhesive Failure
	6.72 MPa	975 psi	Overlap, 71°C water soak for 14 days, Cohesive Failure
	6.89 MPa	1000 psi	Overlap, Antifreeze Coolant, Substrate Failure
	7.24 MPa	1050 psi	Overlap, Diesel Fuel, Substrate Failure
	7.412 MPa	1075 psi	Overlap, PE, Substrate Failure
	7.412 MPa	1075 psi	Overlap, NaOH, Substrate Failure
	7.58 MPa	1100 psi	Overlap, HDPE, Substrate Failure
	7.58 MPa	1100 psi	Overlap, PP, Substrate Failure
	7.58 MPa	1100 psi	Overlap, Control, Substrate Failure
	7.58 MPa	1100 psi	Overlap, RT salt water soak for 14 days, Substrate Failure
	7.58 MPa	1100 psi	Overlap, HCl, Substrate Failure
	10.3 MPa	1500 psi	Overlap, Gel Coat (3/16" thick), Substrate Failure
	10.51 MPa	1525 psi	Overlap, ABS, Substrate Failure
	14.1 MPa	2050 psi	Overlap, PVC, Substrate Failure
	14.8 MPa	2150 psi	Overlap, Oily HDG, Cohesive Failure
	15.69 MPa	2275 psi	Overlap, Copper (1/16" thick), Cohesive Failure
	15.69 MPa	2275 psi	Overlap, Aluminum (1/16" thick), Cohesive Failure
	15.9 MPa	2300 psi	Overlap, 304 Stainless Steel (1/32" thick), Cohesive Failure
	17.06 MPa	2475 psi	Overlap, Green FRP, Cohesive Failure
	17.2 MPa	2500 psi	Overlap, CRS (1/32" thick), Adhesive Failure
	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap
	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, HDPE, Cohesive Failure
	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, Green FRP, AF/CF
	3.28 MPa @Temperature 66.0 °C	475 psi @Temperature 151 °F	Overlap, Green FRP, AF/CF
	3.45 MPa @Temperature 66.0 °C	500 psi @Temperature 151 °F	Overlap, HDPE, Cohesive Failure
	4.83 MPa @Temperature 49.0 °C	700 psi @Temperature 120 °F	Overlap, HDPE, Cohesive Failure
	4.83 MPa @Temperature 49.0 °C	700 psi @Temperature 120 °F	Overlap, Green FRP, Cohesive Failure
	5.17 MPa @Temperature -29.0 °C	750 psi @Temperature -20.2 °F	Overlap, HDPE, Cohesive Failure
	6.03 MPa @Temperature -29.0 °C	875 psi @Temperature -20.2 °F	Overlap, Green FRP, Cohesive Failure
	7.58 MPa @Temperature 23.0 °C	1100 psi @Temperature 73.4 °F	Overlap, HDPE, Substrate Failure
	7.58 MPa @Temperature 23.0 °C	1100 psi @Temperature 73.4 °F	Overlap, Green FRP, Substrate Failure
	16.5 MPa @Temperature 24.0 °C	2400 psi @Temperature 75.2 °F	Overlap
Peel Strength	1.75 kN/m	10.0 pli	T-Peel
	2.98 kN/m	17.0 pli	T-Peel, HDPE, Substrate Failure

Thermal Properties	Metric	English	Comments
CTE, linear	125 µm/m-°C	69.4 µin/in-°F	Below Tg
	170 µm/m-°C	94.4 µin/in-°F	Above Tg
Glass Transition Temp, Tg	33.0 °C	91.4 °F	onset

Processing Properties	Metric	English	Comments
Cure Time	180 min	3.00 hour	Time to Handling Strength

Descriptive Properties	Value	Comments
Appearance	Amber	Base
	White	Accelerator
	Yellow