SABIC Innovative Plastics LNP THERMOCOMP MB008S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MB008S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MB008S is a compound based on Polypropylene resin containing 40% Glass Bead. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.012 - 0.014 cm/cm @Time 86400 sec |
0.012 - 0.014 in/in @Time 24.0 hour |
ASTM D955 |
| 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ASTM D955 |
| 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| 15.0 MPa | 2180 psi | ISO 527 | |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
| 19.0 MPa | 2760 psi | ISO 527 | |
| Elongation at Break | 43.8 % | 43.8 % | ISO 527 |
| 160 % | 160 % | ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| 6.1 % | 6.1 % | ISO 527 | |
| Tensile Modulus | 1.66 GPa | 241 ksi | 1 mm/min; ISO 527 |
| 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 27.0 MPa | 3920 psi | ASTM D790 |
| 36.0 MPa | 5220 psi | ISO 178 | |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D790 |
| 2.20 GPa | 319 ksi | ISO 178 | |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.61 J/cm | 4.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.20 µm/m-°C @Temperature -40.0 - 40.0 °C |
4.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 76.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 7.20 µm/m-°C @Temperature -40.0 - 40.0 °C |
4.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 66.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 102 °C @Thickness 3.20 mm |
216 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 60.0 °C @Thickness 3.20 mm |
140 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nitriflex N-7420P NBR / PVC
- Victrex® PEEK 600PF Polyetheretherketone (discontinued **)
- SABIC Innovative Plastics Lexan® CFR9131 PC COPOLYMER (Asia Pacific)
- Huntsman IROGRAN® A 92 K 5031 TPU-High Temperature Performance
- Karina E 630-10/175-A-IS White PVC Compound
- SSAB Tunnplat Domex® 420YP Cold-forming Steel, HSLA
- Samyang Tribit® 1501N PBT, Flame Retardancy
- Teknor Apex Sinvicomp SIH 5009 Polyvinyl Chloride, Flexible
- Arlon 44571R010 0.011" (0.279 mm) Uncured Silicone Rubber with Fiberglass Substrate
- LG Chemical 15NFI GPPS
Copyright © lookpolymers.com All Rights Reserved