- Nylon 66, 40% Glass Fiber Filled
- Arkema Group Orgalloy® RS 6635 A Polyamide 6.6 Alloy 35% Glass Fiber reinforced
Arkema Group Orgalloy® RS 6635 A Polyamide 6.6 Alloy 35% Glass Fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® RS 6635 A Polyamide 6.6 Alloy 35% Glass Fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Rigid grade, Nylon 6.6 basedMolding of Engineering PartsInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO R1183 |
| Water Absorption | 0.40 % | 0.40 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 23°C / 50% RH; ISO 62 |
| 1.9 % | 1.9 % | in 23°C water; ISO 62 | |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | ISO 868 |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | ISO R527 |
| Elongation at Break | 3.4 % | 3.4 % | ISO R527 |
| Modulus of Elasticity | 9.60 GPa | 1390 ksi | ISO R527 |
| Flexural Strength | 240 MPa | 34800 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| Charpy Impact, Notched | 2.25 J/cm² | 10.7 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 20.0 J/cm² @Temperature -20.0 °C |
95.2 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 9320 MPa | 1.35e+6 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.0 µm/m-°C @Temperature 20.0 - 60.0 °C |
9.44 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 - 60.0 °C |
55.6 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| Melting Point | 255 °C | 491 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO R75 |
| Vicat Softening Point | 200 °C | 392 °F | 50 N - B method; ISO 306 |
| >= 230 °C | >= 446 °F | 10 N - A method; ISO 306 | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.90e+15 ohm-cm | 1.90e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 4.80e+15 ohm | 4.80e+15 ohm | ASTM D257 |
| Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm |
864 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Dissipation Factor | 0.015 @Frequency 100000 Hz |
0.015 @Frequency 100000 Hz |
NFC 26 230 |
| 0.030 @Frequency 100 Hz |
0.030 @Frequency 100 Hz |
NFC 26 230 | |
| 0.031 @Frequency 1000 Hz |
0.031 @Frequency 1000 Hz |
NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive classification | B-3 | FMVSS 302 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1945 TPE, PP Overmold or Standalone use
- Solvay Chemicals SOLKANE® 227 pharma
- Samsung Cheil Industries Starex® SV-0165 U ABS, Unreinforced Extrusion Grade
- Stir SpA SR 80 2 (PVC)
- Trelleborg Hypalon® H730 Chlorosulphonated Polyethylene
- Eagle Brass 70265 XP175, 1/2 Hard
- Dow Corning SYL-OFF® PMCP7016 Crosslinker
- Aremco Pyro-Putty™ 2500 High Temperature Ceramic-Metallic Putty, Iron Oxide Filled
- 3M Dyneon™ Aflas® FA-100H PTFE Fluoroelastomer (discontinued **)
- Total Finathene® 50100.3 HDPE blow molding (discontinued **)
Copyright © lookpolymers.com All Rights Reserved