Arkema Group Orgalloy® RS 6015 BV Nylon 6 Alloy, Glass Fiber + Bead Filled (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® RS 6015 BV Nylon 6 Alloy, Glass Fiber + Bead Filled (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.RS 6015BV: 15 % glass fiber, 10 % glass beads for profile extrusion (low distortion, isotropy, aspect)ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³
Water Absorption	2.5 %	2.5 %
Moisture Absorption at Equilibrium	1.0 %	1.0 %	Humidity Absorption
Melt Flow	3.0 g/10 min @Load 2.16 kg, Temperature 235 °C	3.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	87.0 MPa	12600 psi	5 mm/min
Elongation at Break	4.5 %	4.5 %	5 mm/min
Tensile Modulus	3.51 GPa	509 ksi	1 mm/min

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	62.0 µm/m-°C @Temperature 20.0 °C	34.4 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	70.0 µm/m-°C @Temperature 20.0 °C	38.9 µin/in-°F @Temperature 68.0 °F
Melting Point	220 °C	428 °F	10°C/min
Deflection Temperature at 0.46 MPa (66 psi)	210 °C	410 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm
Dielectric Constant	2.6 @Frequency 100 Hz	2.6 @Frequency 100 Hz
	3.4 @Frequency 1e+6 Hz	3.4 @Frequency 1e+6 Hz
Dielectric Strength	34.0 kV/mm	864 kV/in
Dissipation Factor	0.023 @Frequency 1e+6 Hz	0.023 @Frequency 1e+6 Hz
	0.064 @Frequency 100 Hz	0.064 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V