Arkema Group LOTADER® 3200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride

Category Polymer , Thermoplastic , EMAAA Terpolymer
Manufacturer Arkema
Trade Name LOTADER®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group LOTADER® 3200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LOTADER 3200 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Due to its properties, LOTADER 3200 is used in pipeline protective coatings as a bonding layer between epoxy resin and polyethylene. LOTADER 3200 is also use as a coupling agent in mineral filled compounds.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 0.940 g/cc

@Temperature 23.0 °C
0.0340 lb/in³

@Temperature 73.4 °F
ISO 1183
Butyl Acrylate Content 6.0 %
6.0 %
IRTF (internal)
Melt Index of Compound 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 46
46
ASTM D2240
Tensile Strength at Break 12.0 MPa
1740 psi
ASTM D638
Elongation at Break 600 %
600 %
ASTM D638
Flexural Modulus 0.120 GPa
17.4 ksi
ASTM D638
Thermal Properties Metric English Comments
Melting Point 107 °C
225 °F
DSC
Vicat Softening Point 80.0 °C

@Load 0.999 kg
176 °F

@Load 2.20 lb
ASTM D1525
Brittleness Temperature <= -50.0 °C
<= -58.0 °F
ASTM D726
Processing Properties Metric English Comments
Die Temperature 180 - 230 °C
356 - 446 °F
Descriptive Properties Value Comments
Maleic Anhydride Content (%) 3.1
IRTF (internal)