Arkema Group Kynar® 4000 HD PVDF  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Kynar® 4000 HD PVDF  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 12086-PVDF-E,GG1N,Q.?E5.I.B.E.C,, ?(6-10)Kynar PVDF are fluorinated thermoplastic homopolymers.Outstanding characteristics of Kynar: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermomechanical properties.Main applications of Kynar: corrosion protection in the chemical industry, coating (painting, coextrusion), off shore, wire and cable.Kynar 4000 HD is a grade of granules for extrusion of thin walled parts, film extrusion and injection molding.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
Water Absorption 0.030 %
0.030 %
Moisture Absorption at Equilibrium 0.015 %
0.015 %
Humidity Absorption
Melt Flow 4.5 g/10 min

@Load 5.00 kg,
Temperature 230 °C
4.5 g/10 min

@Load 11.0 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 52.0 MPa
7540 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 9.0 %
9.0 %
50 mm/min
Tensile Modulus 2.20 GPa
319 ksi
1 mm/min
Charpy Impact Unnotched 25.5 J/cm²
121 ft-lb/in²
22.2 J/cm²

@Temperature -30.0 °C
106 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 150 µm/m-°C

@Temperature 20.0 °C
83.3 µin/in-°F

@Temperature 68.0 °F
Melting Point 171 °C
340 °F
10°C/min
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
Vicat Softening Point 139 °C
282 °F
50°C/hr; 50N
Glass Transition Temp, Tg -40.0 °C
-40.0 °F
10°C/min
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Oxygen Index 80.7 %
80.7 %
Electrical Properties Metric English Comments
Dielectric Constant 7.2

@Frequency 1e+6 Hz
7.2

@Frequency 1e+6 Hz
9.9

@Frequency 100 Hz
9.9

@Frequency 100 Hz
Dissipation Factor 0.030

@Frequency 100 Hz
0.030

@Frequency 100 Hz
0.226

@Frequency 1e+6 Hz
0.226

@Frequency 1e+6 Hz