Arkema Group Kynar® 1000 HDC N 118 PVDF (discontinued **)

Category	Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Kynar® 1000 HDC N 118 PVDF (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation ISO 12086-PVDF-E,GG1C,P.?E5.I.B.E.C,, ?(1.5-2.5)Kynar PVDF are fluorinated thermoplastic homopolymers.Outstanding characteristics of Kynar: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermomechanical properties.Main applications of Kynar: corrosion protection in the chemical industry, coating (painting, coextrusion), off shore, wire and cable.Kynar 1000 HDC N 118 has the same properties than Kynar 1000 HD and is used in the same applications (compression and transfer molding, extrusion of thick walled parts: blocks, rods, plaques, tubes) but is black colored.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.77 g/cc	0.0639 lb/in³
Melt Flow	1.1 g/10 min @Load 5.00 kg, Temperature 230 °C	1.1 g/10 min @Load 11.0 lb, Temperature 446 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	52.0 MPa	7540 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	9.0 %	9.0 %	50 mm/min
Tensile Modulus	2.00 GPa	290 ksi	1 mm/min

Thermal Properties	Metric	English	Comments
Melting Point	169 °C	336 °F	10°C/min
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in

Electrical Properties	Metric	English
Dielectric Constant	6.4 @Frequency 1e+6 Hz	6.4 @Frequency 1e+6 Hz
	9.5 @Frequency 100 Hz	9.5 @Frequency 100 Hz
Dissipation Factor	0.069 @Frequency 100 Hz	0.069 @Frequency 100 Hz
	0.246 @Frequency 1e+6 Hz	0.246 @Frequency 1e+6 Hz