Arkema Group Appryl® HXN 1240 Polypropylene, 40% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Arkema |
| Trade Name | Appryl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Appryl® HXN 1240 Polypropylene, 40% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Compound of a PP homopolymer and 40% talc, warm stabilized suitable for under hood automotive applications.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50 mm/min |
| Elongation at Break | 8.0 % | 8.0 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min |
| Tensile Modulus | 3.12 GPa | 453 ksi | 1 mm/min |
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | |
| 1.10 J/cm² @Temperature -30.0 °C |
5.24 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | |
| Vicat Softening Point | 91.0 °C | 196 °F | 50°C/hr; 50N |
Users viewing this material also viewed the following:
- Outokumpu 4372 Cr-Ni Austenitic Stainless Steel
- ExxonMobil Escorene® LX-0252 LMDPE Rotational Molding Grade (discontinued **)
- Star Plastics PC/PBTQX7008 Molding Grade PC/PBT
- Techmer ES Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12
- Samsung Cheil Industries Infino® TK-2046H PCT, Glass Filled
- Saint-Gobain CHR® 2255-2 High Modulus PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- ExxonMobil Hicor® 30 HT 103 OHD Film
- Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness)
- BASF Neopolen® P 9435 0.07 g/cc Core density; Expanded Polypropylene (Europe)
- Total Finathene® CD 481 HDPE conduit (discontinued **)
Copyright © lookpolymers.com All Rights Reserved