- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Samsung Cheil Industries Starex® WR-9310 ASA, Unreinforced Heat Resistant
Samsung Cheil Industries Starex® WR-9310 ASA, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WR-9310 ASA, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat resistant ASA that is used in the interior/exterior material of automobileInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 45.1 MPa | 6540 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 58.8 MPa | 8530 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 3.43 J/cm @Thickness 3.17 mm |
6.43 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Americas Styrenics Styron® 489M High Impact Polystyrene (discontinued **)
- Magyar Aluminum ALOLT 1AF Aluminum Hydroxide
- Kostat 7440 Conductive ABS Compound
- Teknor Apex Sinvicomp SME 8510 Polyvinyl Chloride, Flexible
- Total PPH 3271 Polypropylene, Oriented Film Extrusion Grade
- A. Schulman POLYFLAM™ RABS 930-01
- ELM® Concrete/Asphalt WS Biodegradable Form Release Agent
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 30% Cold Rolled (UNS S30400)
Copyright © lookpolymers.com All Rights Reserved