Aremco Aremco-Bond™ 2315 High Performance Epoxide
| Category | Polymer , Thermoset , Epoxy |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 2315 High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Temperature, Low Viscosity, Potting Compound for Electrical Applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.95 g/cc | 1.95 g/cc | |
| Viscosity | 3000 cP | 3000 cP | Mixed Viscosity |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 92 | 92 | |
| Flexural Strength | 84.8 MPa | 12300 psi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 34.2 µm/m-°C @Temperature 20.0 °C |
19.0 µin/in-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 1.21 W/m-K | 8.40 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 185 °C | 365 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |
| Shrinkage | 0.30 % | 0.30 % | Cure Shrinkage |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 4.7 @Frequency 1000 Hz |
4.7 @Frequency 1000 Hz |
|
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | |
| Dissipation Factor | 0.010 | 0.010 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 240 min | 4.00 hour | 2 hrs at 160°F; 2 hrs at 300°F (Recommended Cure) |
| 360 min @Temperature 121 °C |
6.00 hour @Temperature 250 °F |
Alternate Cure | |
| Pot Life | 120 min @Temperature 25.0 °C |
120 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Excellent | |
| Color | Black | |
| Mix Ratio By Weight | 100:25 | resin:hardener |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3653T TPE, PP Overmold or Standalone use
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N220 Filler
- Manifattura Cattaneo PA 6.6 30% GF Nylon, Glass Filled
- Borealis Borecene™ RM8343PL Linear Polyethylene for Rotational Molding
- A. Schulman POLYBATCH™ Cream 90059 Concentrate Based In Polyethylene
- Total MDPE HR 515 Medium Density Polyethylene, Blown Film
- Trelleborg Emerson & Cuming Stycast® E 1400 Two-Component General Purpose Encapsulant
- Chosun Refractories N2-1 Fireclay brick
- ExxonMobil Fenso 71
Copyright © lookpolymers.com All Rights Reserved