Amity Thermosets ATS 158 Phenolic Molding Glass fiber Filler, Compression Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATS 158 Phenolic Molding Glass fiber Filler, Compression Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Ammonia free Increased CTI High electrical insulation properties High mechanical strength Temperature stability (230 0 C) Color-black Medium flow Applications:Switchgear componentCommutators (washing machine, motors, vacuum cleaner, electrical tools and large commutators )Automotive components ( electrical ), etc. Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.80 - 1.85 g/cc
0.0650 - 0.0668 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.750 - 0.850 g/cc
0.0271 - 0.0307 lb/in³
IS 867-1963
Water Absorption 0.10 - 0.20 %
0.10 - 0.20 %
IS 13411-1993
Linear Mold Shrinkage 0.00050 - 0.0020 cm/cm
0.00050 - 0.0020 in/in
IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break >= 60.0 MPa
>= 8700 psi
5 mm/min.; IS 867-1963
Shear Strength >= 110 MPa
>= 16000 psi
2mm/min.; IS 867-1963
Izod Impact, Notched >= 0.480 J/cm
>= 0.899 ft-lb/in
IS 13411-1992
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 230 °C
446 °F
2 hours
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+12 ohm-cm
>= 1.00e+12 ohm-cm
IS 3396-1979
Surface Resistance >= 1.00e+11 ohm
>= 1.00e+11 ohm
IS 3396-1979
Dielectric Strength >= 10.0 kV/mm

@Temperature 90.0 °C
>= 254 kV/in

@Temperature 194 °F
IS 2584-1963
Comparative Tracking Index >= 175 V
>= 175 V
2824-1975
Processing Properties Metric English Comments
Mold Temperature 160 - 180 °C
320 - 356 °F
Injection Pressure 15.68 - 34.3 MPa
2274 - 4970 psi
Mold Pressure
Cure Time 0.833 - 1.17 min
0.0139 - 0.0194 hour
per mm
Shelf Life 4.00 Month
4.00 Month
10-25°C
Descriptive Properties Value Comments
Ammonia content Nil