Amity Thermosets ATE 183 Phenolic Molding Mica and organic Filler, Compression Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets ATE 183 Phenolic Molding Mica and organic Filler, Compression Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:Electric low loss Low water absorption Low shrinkage Heat stableGlossy surface finishVery good mouldabilityGood electrical insulationGood chemical resistantColor-blackMedium flowApplications: Electric motor commutators ( medium mechanical strength )Motor starter partsSignaling equipment partsHigh voltage electric meter coversCircuit protecting switchesElectric relay parts which ought to withstand high voltage Automotive parts ( spacers, spark plugs etc )Components which ought to withstand electric shock but not high mechanical stressComponents which ought to be dimensionally stable electrically insulating & resistant to humidity, etc. Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.68 - 1.78 g/cc	0.0607 - 0.0643 lb/in³	Molding; IS 867-1963
Apparent Bulk Density	0.700 - 0.850 g/cc	0.0253 - 0.0307 lb/in³	IS 867-1963
Water Absorption	0.12 - 0.25 %	0.12 - 0.25 %	IS 13411-1993
Linear Mold Shrinkage	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	30.0 - 45.0 MPa	4350 - 6530 psi	5 mm/min.; IS 867-1963
Shear Strength	50.0 - 65.0 MPa	7250 - 9430 psi	IS 867-1963
Izod Impact, Notched	0.150 - 0.250 J/cm	0.281 - 0.468 ft-lb/in	IS 13411-1992

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 - 1.00e+13 ohm-cm	1.00e+12 - 1.00e+13 ohm-cm	IS 3396-1979
Surface Resistance	3.2e+11 - 1.0e+12 ohm	3.2e+11 - 1.0e+12 ohm	IS 3396-1979
Dielectric Strength	8.00 - 10.5 kV/mm @Temperature 90.0 °C	203 - 267 kV/in @Temperature 194 °F	IS 2584-1963

Processing Properties	Metric	English	Comments
Mold Temperature	160 - 180 °C	320 - 356 °F
Injection Pressure	14.7 - 35.28 MPa	2130 - 5117 psi	Mold Pressure
Cure Time	0.917 - 1.08 min	0.0153 - 0.0181 hour	per mm
Shelf Life	12.0 Month	12.0 Month	10-25°C