Ametek 17-4 P/M Process, Sintered at 2300°F (1260°C)

Category	Metal , Ferrous Metal , Stainless Steel , Precipitation Hardening Stainless
Manufacturer	Ametek
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ametek 17-4 P/M Process, Sintered at 2300°F (1260°C).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Composition reported is typical of 17-4 precipitation hardening stainless. This alloy is widely used because of its high strength, high hardness, excellent corrosion resistance, and easy heat treatment. The 17-4 PH alloy is used in aerospace, medical, food processing, and chemical industries for applications such as pump shafts, valve stems, braces, fasteners, coupling, rocket and missile components, hydraulic actuators, and wear rings.Mechanical property data below is from samples aged for 1 hour at 900°F (482°C) in hydrogen - the H900 condition, which maximizes strength. The properties that can be expected for material that was lubricated with 3/4% Acrawax C and compacted at 48 tsi are shown below.17-4 PH is a registered trademark of Armco, Inc.; information provided by Ametek Specialty Metal Product Division.

Mechanical Properties	Metric	English
Hardness, Rockwell B	105	105
Tensile Strength, Ultimate	900 MPa	131000 psi
Tensile Strength, Yield	660 MPa	95700 psi
Elongation at Break	1.8 %	1.8 %

Component Elements Properties	Metric	English	Comments
Carbon, C	0.035 %	0.035 %
Chromium, Cr	16.3 %	16.3 %
Copper, Cu	4.0 %	4.0 %
Iron, Fe	74 %	74 %	as balance
Manganese, Mn	0.50 %	0.50 %
Nickel, Ni	4.0 %	4.0 %
Niobium, Nb (Columbium, Cb)	0.30 %	0.30 %
Phosphorous, P	0.020 %	0.020 %
Silicon, Si	0.50 %	0.50 %
Sulfur, S	0.015 %	0.015 %