Albis Plastics Cellulose Acetate CA700 , Unreinforced, 35% Plasticizer (discontinued **)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Albis Plastics Cellulose Acetate CA700 , Unreinforced, 35% Plasticizer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amorphous Cellulose Acetate (CA)Characteristics: Chemical Resistance, Toughness, Strength, Hardness, Gloss, Clarity and "Feel"Applications: Tool Handles, Optical Products, Toys and Sheet ProductsProcessing: Injection Molding (Melt Temperature: 470°F, Mold Temperature: 160°F)Data supplied by ALBIS Plastics Corporation.

Physical Properties	Metric	English	Comments
Density	1.26 g/cc	0.0455 lb/in³	ASTM D792
Water Absorption	2.4 %	2.4 %	(24 hr); ASTM D570
Linear Mold Shrinkage	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	29.6 MPa	4290 psi	ASTM D638
Tensile Strength, Yield	25.5 MPa	3700 psi	ASTM D638
Flexural Yield Strength	33.8 MPa	4900 psi	ASTM D790
Flexural Modulus	1.31 GPa	190 ksi	ASTM D790
Izod Impact, Notched	2.24 J/cm	4.20 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	57.0 °C	135 °F	ASTM D648
Vicat Softening Point	95.0 °C	203 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	213 °C	415 °F	Injection Molding
Mold Temperature	43.0 °C	109 °F