DuPont Performance Polymers VTR 8505/8500 Formulation (discontinued **)
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers VTR 8505/8500 Formulation
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationViton® 8505
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 51 @Temperature 121 °C |
51 @Temperature 250 °F |
ML-10 (gum)-Akron data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 67 | 67 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 18.2 MPa | 2640 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 298 % | 298 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00390 GPa | 0.566 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 20 % @Temperature 200 °C |
20 % @Temperature 392 °F |
Method B, O-rings 70 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -32.9 °C | -27.2 °F | DSC, modulated |
Users viewing this material also viewed the following:
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with Paraplex G25
- Fainplast Compounds RE 520/1 Rigid PVC, Extrusion
- Huntsman Tactix 742 Epoxy
- Lotte Chemical Titan TITANPRO® PM803 Polypropylene homopolymer
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Toyobo PELPRENE™ PE450B Polyester TPE
- EMS-Grivory Grivory® LV-30H FWA black 9225 PA12-GF30
- Carmel Olefins CAPILENE® T 77 A Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved