Aclo Accutech Polypropylene Homopolymer HP0339W40L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339W40L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 4.000 GPa | 580.1 ksi | ASTM D638 |
| Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
| Flexural Modulus | 4.200 GPa | 609.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.278 J/cm | 0.520 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F |
Users viewing this material also viewed the following:
- MV Labs BA800 BaC2O4 Barium oxalate
- Kinlead LSD12 Low Temperature Grade Heat Sealable Film (thickness: 20 µm)
- Lubrizol Advanced Materials Pearlbond® DAP 750/2 Thermoplastic Polyurethane
- SABIC Innovative Plastics Xenoy® 1760T PBT+PC (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Red 5557 Concentrate Based In Polyethylene
- A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black
- Loctite® Assure™ 425 Threadlocker
- Eagle Brass 510 Phosphor Bronzes 5% A, 3/4 Hard
Copyright © lookpolymers.com All Rights Reserved