Aclo Accutech Polypropylene Homopolymer HP0339T30L Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339T30L Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 84 | 84 | ASTM D785 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Elongation at Break | 14 % | 14 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.299 GPa | 333.5 ksi | ASTM D638 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.251 J/cm | 0.470 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.2 °C | 144 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible 90453 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Asahi Kasei Tenac® 5012 Acetal Homopolymer (discontinued **)
- Gouda Vuurvast B Sp Dense Refractory Brick
- Sylvin Technologies 8925-85 Natural PVC Extrusion Compound
- A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
- Vicone High Performance Rubber VicoFluor™ 57FK-GR High Performance Fluoroelastomer Rubber
- BASF Ultramid® 1C PA6/66 (Conditioned)
- Azoty Tarnow™ Tarnamid® T-27 MW30 Polyamide 6 - Mineral Reinforced
- Alcoa KAMA 3200 Prime High Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved