SABIC Innovative Plastics Lexan® 4501 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polyphthalate Carbonate |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® 4501 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LEXAN 4501 is a copolymer of polyphthalate carbonate resin for applications requiring high heat resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 300 °C |
10 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ISO 2039-2 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*3; ISO 180/1A |
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 5.90 J/cm² | 28.1 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft²-°F | ISO 8302 |
| Vicat Softening Point | 160 °C | 320 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.024 @Frequency 100 Hz |
0.024 @Frequency 100 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- LATI LATILUB 88/50-20GRT K/10 PEEK Based, 10% Carbon Fiber Reinforced, 20% Graphite and PTFE Self Lubricating Plastic
- LyondellBasell Microthene® F FA70900 High Density Polyethylene
- LG Chemical LUMID HI2152A(W) PA6+GF15%, High Impact
- MBA Polymers PP 2131 F20 Post-consumer recycled polypropylene copolymer with approximately 20% fillers
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR Thanecure® ZM
- Cyclics CBT® 100 Thermoplastic Resin
- PolyOne Synprene® RT-4060 Thermoplastic Elastomer - SBC, Mineral Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved