Aclo Accutech Polycarbonate POL051G10L Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polycarbonate POL051G10L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | MD; ASTM D955 |
| Melt Flow | 11 g/10 min | 11 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ASTM D638 |
| Tensile Strength, Yield | 75.01 MPa | 10880 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.699 GPa | 391.5 ksi | ASTM D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm | 1.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F |
Users viewing this material also viewed the following:
- BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Polimeri Europa Intol® 1723 Emulsion Styrene-Butadiene Rubber
- ICO Polymers ICORENEâ„¢ 115-3561 LMDPE Rotational Molding Resin
- Greene Tweed CHEMRAZ® SD625 Perfluoroelastomer
- Johnson Matthey JM6337 Soft Solder/Flux
- Techmer ES Elastoblend® PA6 GF33 IM2 BK 33% Glass Filled
- SIDPEC EGYPTENE® HD 5211 EA HDPE Injection Molding
- Saint-Gobain Norton® V760 High Density Vibration
- Asahi Kasei Thermylene® P6-25FG-1734 25% Glass Fiber Reinforced, High Impact
- Chosun Refractories HACT-165 High Alumina Castables
Copyright © lookpolymers.com All Rights Reserved