- Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- Aclo Accutech ABS ABS834G20L Glass Reinforced
Aclo Accutech ABS ABS834G20L Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech ABS ABS834G20L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 87 | 87 | ASTM D785 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 3.499 GPa | 507.5 ksi | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 4.599 GPa | 667.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F |
Users viewing this material also viewed the following:
- LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**)
- Gwent Electronic Materials C2080211P2 High Brightness Phosphor Ink (Blue/Green & Blue)
- Karina E 74/240-D-IS-SD-TR Compound PVC Crystal
- Schott BG38 Band Pass Filter
- Tisan TISLAMID® 66 UNR Nylon 66
- A. Schulman PP 1901-01 Polypropylene High-Flow Homopolymer Polypropylene
- Trelleborg Commercial Neoprene® C801 Chloroprene
- Amco PRIMATOP HDPE 006964EG Pipe Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved