Aclo Accuguard Polypropylene CP1467V2CSL Copolymer Flame Retardant Copper Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Aclo Compounders |
| Trade Name | Accuguard |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accuguard Polypropylene CP1467V2CSL Copolymer Flame Retardant Copper Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 200 MPa | 29000 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Modulus | 1.100 GPa | 159.5 ksi | ASTM D638 |
| Flexural Strength | 33.0 MPa | 4790 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 77.8 °C | 172 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.8 °C | 118 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0625 in |
UL File #E99379 |
Users viewing this material also viewed the following:
- Polykemi AB SCANMID 6 B12^ FX30 Nylon 6, Glass Fiber Reinforced
- KaMin Nucap® 100G Kaolin Clay - Surface Treated
- Polyplastics Duranex® 313RA Polybutylene Terephthalate (PBT), Resin adhesion improved for multiple injection molding, 15% GF filled
- A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- ExxonMobil 846 Mobil DTE 800 Series
- Covestro Bayblend® KU 2-1468 Polycarbonate/ABS Blend
- Aclo Accutech Polypropylene Homopolymer HP0339M40L Mica Reinforced
- Kazanorgsintez PE2NT 11-285D High Density Polyethylene Composite
- LNP ULTEM® SMU5836 Polyetherimide, 30% Carbon Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved