- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Aclo Accucomp ABS ABS846HL High Flow Medium Impact Grade
Aclo Accucomp ABS ABS846HL High Flow Medium Impact Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Aclo Compounders |
| Trade Name | Accucomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accucomp ABS ABS846HL High Flow Medium Impact Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | MD; ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 1.700 GPa | 246.5 ksi | ASTM D638 |
| Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 3.42 J/cm | 6.40 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL File #E56070 |
Users viewing this material also viewed the following:
- MV Labs CA880 Ca(OH)2 Calcium hydroxide
- OCTAL DPET™ PET Sheet
- SABIC Innovative Plastics Lexan® IR 2210 PC (Europe-Africa-Middle East)
- Total Evatane® 28 - 03 HDPE, blown film (discontinued **)
- Lucite International Diakon® ST50G8 Toughened Acrylic Polymer
- Stir SpA SPI 65 (PVC)
- UBE UBEPOL BR150L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C)
- CeramTec MZ 429 Zirconia, ZrO2-Y2O3
- ArcelorMittal Dual Phase 780 LCE Y500 Very high strength steel, Cold Rolled Steel
Copyright © lookpolymers.com All Rights Reserved